Vacuum plates from light-colored rubber.

Non-shaped (roll) – thickness up to 6 mm, width up to 1,000 mm, length not less than 1,000 mm.

Shaped (sheet) – thickness from 2 to 50 mm in sheets of size 500 * 500 mm, 720 * 720 mm, 750 * 750 mm

It is made in rolls up to 1,000 mm wide, up to 6 mm thick, and in sheets 500 * 500 mm, 720 * 720 mm, 750 * 750 mm up to 50 mm thick

Roll technical conductive plate (TU 38.105190-76)

Scope: It is intended for removal of charges of static electricity.

Working environment: Air of premises, capacities, vessels; nitrogen, inert gases at pressures from 0.05 to 0.4 MPa.

Note: Electrical resistivity is in the range 1 * 102 – 5 * 105 Ohms.

Scope: For the parts working at a pressure of 2.45-2.94 MPa (25-30 kg / cm2) at a temperature from -4 ° C to + 35 ° C.

Processing medium: Sea water. Pressure no more than 0.98 MPa (10 kg / cm2).

• Scope: It is intended for the manufacture of rubber products used to seal fixed joints, prevent friction between metal surfaces, to perceive single shock loads, and also as gaskets, decks and other non-sealing joints.Working environment: Air of premises, capacities, vessels; inert gases at a pressure of 0.05 to 0.4 MPa or oil, petroleum-based fuels, gasoline at a pressure of 0.05 to 10.0 MPa; nitrogen. Temperature from -30 ° С to + 80 ° СNote: A plate longer than 5000 mm is supplied as agreed with the customer.

   

  Technical Characteristics
  Type	Shore Hardness	Thickness (mm)	Length (mm)	Width (mm)
  OPR (soft)	40-55	2,0-6,0	from 500	from 300
  OPR (medium hard)	55-70	2,0-6,0	Uo-to 5000 (rolls)	Up-to 1200
  OPR (hard)	70-90	1,5-2,0	Up-to 5000	(rolls) up-to 1200

Scope: It is intended for the manufacture of rubber products used to seal fixed joints, prevent friction between metal surfaces, to perceive single shock loads, and also as gaskets, decks and other non-sealing joints.

Working environment: Air of premises, capacities, vessels; nitrogen, inert gases at a pressure of 0.05 to 0.4 MPa or fresh, marine, industrial, waste water without organic solvents and lubricants; salt solution with a concentration up to the saturation limit; acids, alkalis with a concentration of not more than 20% at a pressure of 0.05 to 10.0 MPa. Temperature from -45 ° С to + 80 ° С.

Note: A plate longer than 5000 mm is supplied as agreed with the customer.

Rubber fabric plate (type II) and rubber (type I) heat and frost acid and alkali resistant (GOST 7338-90)

Scope: It is intended for the manufacture of rubber products used to seal fixed joints, prevent friction between metal surfaces, to perceive single shock loads, and also as gaskets, decks and other non-sealing joints.

Working environment: Air of premises, capacities, vessels; nitrogen, inert gases at a pressure of 0.05 to 0.4 MPa or fresh, marine, industrial, waste water without organic solvents and lubricants; salt solution with a concentration up to the saturation limit; acids, alkalis with a concentration of not more than 20% at a pressure of 0.05 to 10.0 MPa. Temperature from -45 ° С to + 80 ° С.